CSB issues safety alert stemming from fatal Tesoro Anacortes investigation
The US Chemical Safety Board (CSB) issued a safety alert entitled “CSB Safety Alert: Preventing High Temperature Hydrogen Attack (HTHA)” focused on preventing accidents similar to the fatal 2010 explosion and fire at the Tesoro Refinery in Anacortes, WA that resulted in 7 worker fatalities.
The CSB’s investigation into the catastrophic failure of a forty-year-old heat exchanger at the Tesoro Refinery determined that the explosion and fire was caused by a damage mechanism known as high temperature hydrogen attack (HTHA) which severely cracked and weakened the carbon steel heat exchanger over time, leading to a rupture. The CSB’s report, released in May 2014, concluded that the standard industry uses for determining vulnerability of equipment to HTHA is inadequate. To address its findings, the CSB made recommendations intended to prevent HTHA to the industry group that issues guidance on HTHA, the American Petroleum Institute (API).
Chairperson Vanessa Allen Sutherland said, “The CSB is concerned that the risk of equipment failure due to HTHA may not be fully known or appreciated within the industry. Our goal is to help inform and educate industry of potential risk in order to prevent future accidents and to protect workers and the public.”
Updated guidance covering this issue - recently published by API - provides incremental improvements, but it fails to address important elements of the CSB’s recommendations. The standard uses what are referred to as “Nelson Curves” to predict the operating conditions where HTHA can occur in different types of steels. The curves are based on process data voluntarily reported to API, and are drawn beneath reported occurrences of HTHA to indicate the “safe” and “unsafe” operating regions.
API’s updated carbon steel Nelson Curves do not take into account all of the estimated process conditions where the catastrophic failure occurred due to HTHA at the Tesoro Anacortes Refinery. As a result, the new curves allow refinery equipment to operate at conditions where HTHA severely damaged the Tesoro heat exchanger. The use of a curve not incorporating significant failure data could result in future catastrophic equipment ruptures.
Because of these noted deficiencies, the Board designated the Recommendation 2010-08-I-WA-R10 with the status of Closed – Unacceptable Action.
Chairperson Vanessa Allen Sutherland said, “In the absence of industry guidance that incorporates findings from the Tesoro Anacortes failure, the CSB is issuing a safety alert to provide additional direction for industry.” The Safety Alert provides the following guidance for industry:
- Identify all carbon steel equipment in hydrogen service that has the potential to harm workers or communities due to catastrophic failure;
- Verify actual operating conditions (hydrogen partial pressure and temperature) for the identified carbon steel equipment;
- Replace carbon steel process equipment that operates above 400 °F and greater than 50 psia hydrogen partial pressure; and
- Use inherently safer materials, such as steels with higher chromium and molybdenum content.
The CSB is an independent federal agency charged with investigating serious chemical accidents. The agency's board members are appointed by the president and confirmed by the Senate. CSB investigations look into all aspects of chemical accidents, including physical causes such as equipment failure as well as inadequacies in regulations, industry standards, and safety management systems.
The Board does not issue citations or fines but does make safety recommendations to plants, industry organizations, labor groups, and regulatory agencies.